A series of new poly(arylene ether sulfone)s has been obtained by solution condensation polymerisation starting from 1,5- and 2,6-bis-(4-fluorosulfonyl)naphthalene with various aromatic dihydroxy compounds. The polymers, obtained in quantitative yields, possessed inherent viscosities in the range 0.28-0.68 dl g-1, had good thermal stability (10% weight loss temperatures were above 405 and 420 °C respectively in nitrogen and air) and high glass transition temperatures (in the range 217-258 °C). They have been characterised by elemental and infrared analyses, GPC and wide-angle X-ray diffraction. The properties of these poly(arylene ether sulfone)s have been compared with those of the corresponding poly(arylene ether ketone)s
Effects of the Structure on the Properties of New Poly (arylene ether sulfone)s Containing Naphthalene Units
BOTTINO, Francesco;DI PASQUALE, Giovanna;POLLICINO, Antonino
2003-01-01
Abstract
A series of new poly(arylene ether sulfone)s has been obtained by solution condensation polymerisation starting from 1,5- and 2,6-bis-(4-fluorosulfonyl)naphthalene with various aromatic dihydroxy compounds. The polymers, obtained in quantitative yields, possessed inherent viscosities in the range 0.28-0.68 dl g-1, had good thermal stability (10% weight loss temperatures were above 405 and 420 °C respectively in nitrogen and air) and high glass transition temperatures (in the range 217-258 °C). They have been characterised by elemental and infrared analyses, GPC and wide-angle X-ray diffraction. The properties of these poly(arylene ether sulfone)s have been compared with those of the corresponding poly(arylene ether ketone)sI documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.