Direct laser-reduction of graphene oxide (GO), as a lithography-free approach, has been proveneffective in manufacturing in-plane micro-supercapacitors (MSCs) with fast ion diffusion. However, the power density and the charge/discharge rate are still limited by the relatively low conductivity of electrodes. Here, we report a facile approach by exploiting femtolaser in situ reduction of the hydrated GO and chloroauric acid (HAuCl4) nanocomposite simultaneously, which incorporates both the patterning of rGO electrodes and the fabrication of Au current collectors in a single step. These flexible MSCs boast achievements of one-hundred fold increase in electrode conductivities of up to 1.1 x 10(6) S m(-1), which provide superior rate capability (50% for the charging rate increase from 0.1 V s(-1) to 100 V s(-1)), sufficiently high frequency responses (362 Hz, 2.76 ms time constant), and large specific capacitances of 0.77 mF cm(-2) (17.2 F cm(-3) for volumetric capacitance) at 1 V s(-1), and 0.46 mF cm(-2) (10.2 F cm(-3)) at 100 V s(-1). The use of photo paper substrates enables the flexibility of this fabrication protocol. Moreover, proof-of-concept 3D MSCs are demonstrated with enhanced areal capacitance (up to 3.84 mF cm(-2) at 1 V s(-1)) while keeping high rate capabilities. This prototype of all solid-state MSCs demonstrates the broad range of potentials of thin-film based energy storage device applications for flexible, portable, and wearable electronic devices that require a fast charge/discharge rate and high power density.

High-rate in-plane micro-supercapacitors scribed onto photo paper using in situ femtolaser-reduced graphene oxide/Au nanoparticle microelectrodes

COMPAGNINI, Giuseppe Romano;
2016-01-01

Abstract

Direct laser-reduction of graphene oxide (GO), as a lithography-free approach, has been proveneffective in manufacturing in-plane micro-supercapacitors (MSCs) with fast ion diffusion. However, the power density and the charge/discharge rate are still limited by the relatively low conductivity of electrodes. Here, we report a facile approach by exploiting femtolaser in situ reduction of the hydrated GO and chloroauric acid (HAuCl4) nanocomposite simultaneously, which incorporates both the patterning of rGO electrodes and the fabrication of Au current collectors in a single step. These flexible MSCs boast achievements of one-hundred fold increase in electrode conductivities of up to 1.1 x 10(6) S m(-1), which provide superior rate capability (50% for the charging rate increase from 0.1 V s(-1) to 100 V s(-1)), sufficiently high frequency responses (362 Hz, 2.76 ms time constant), and large specific capacitances of 0.77 mF cm(-2) (17.2 F cm(-3) for volumetric capacitance) at 1 V s(-1), and 0.46 mF cm(-2) (10.2 F cm(-3)) at 100 V s(-1). The use of photo paper substrates enables the flexibility of this fabrication protocol. Moreover, proof-of-concept 3D MSCs are demonstrated with enhanced areal capacitance (up to 3.84 mF cm(-2) at 1 V s(-1)) while keeping high rate capabilities. This prototype of all solid-state MSCs demonstrates the broad range of potentials of thin-film based energy storage device applications for flexible, portable, and wearable electronic devices that require a fast charge/discharge rate and high power density.
File in questo prodotto:
File Dimensione Formato  
1286936high.pdf

accesso aperto

Tipologia: Documento in Pre-print
Licenza: PUBBLICO - Pubblico con Copyright
Dimensione 1.43 MB
Formato Adobe PDF
1.43 MB Adobe PDF Visualizza/Apri
c5ee03637b.pdf

solo gestori archivio

Tipologia: Versione Editoriale (PDF)
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 5.44 MB
Formato Adobe PDF
5.44 MB Adobe PDF   Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11769/29180
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 213
  • ???jsp.display-item.citation.isi??? 200
social impact