Ni-based nanostructures are attractive catalytic materials for many electrochemical applications, among which are non-enzymatic sensing, charge storage, and water splitting. In this work, we clarify the synthesis kinetics of Ni(OH)2/NiOOH nanowalls grown by chemical bath deposition at room temperature and at 50 °C. We applied the results to non-enzymatic glucose sensing, reaching a highest sensitivity of 31 mA cm-2mM-1. Using scanning electron microscopy, x-ray diffraction analysis and Rutherford backscattering spectrometry we found that the growth occurs through two regimes: first, a quick random growth leading to disordered sheets of Ni oxy-hydroxide, followed by a slower growth of well-aligned sheets of Ni hydroxide. A high growth temperature (50 °C), leading mainly to well-aligned sheets, offers superior electrochemical properties in terms of charge storage, charge carrier transport and catalytic action, as confirmed by cyclic voltammetry and electrochemical impedance spectroscopy analyses. The reported results on the optimization and application of low-cost synthesis of these Ni-based nanostructures have a large potential for application in catalysis, (bio)sensing, and supercapacitors areas.

Enhanced sensitivity in non-enzymatic glucose detection by improved growth kinetics of Ni-based nanostructures

URSO, MARIO;Strano, V;Bruno, E;Priolo, F;Mirabella, S
2018-01-01

Abstract

Ni-based nanostructures are attractive catalytic materials for many electrochemical applications, among which are non-enzymatic sensing, charge storage, and water splitting. In this work, we clarify the synthesis kinetics of Ni(OH)2/NiOOH nanowalls grown by chemical bath deposition at room temperature and at 50 °C. We applied the results to non-enzymatic glucose sensing, reaching a highest sensitivity of 31 mA cm-2mM-1. Using scanning electron microscopy, x-ray diffraction analysis and Rutherford backscattering spectrometry we found that the growth occurs through two regimes: first, a quick random growth leading to disordered sheets of Ni oxy-hydroxide, followed by a slower growth of well-aligned sheets of Ni hydroxide. A high growth temperature (50 °C), leading mainly to well-aligned sheets, offers superior electrochemical properties in terms of charge storage, charge carrier transport and catalytic action, as confirmed by cyclic voltammetry and electrochemical impedance spectroscopy analyses. The reported results on the optimization and application of low-cost synthesis of these Ni-based nanostructures have a large potential for application in catalysis, (bio)sensing, and supercapacitors areas.
2018
Nanowalls, nanofoam, catalysis, glucose sensing, self-assembly, chemical bath deposition, low-cost synthesis.
File in questo prodotto:
File Dimensione Formato  
Urso_2018_Nanotechnology_29_165601.pdf

solo gestori archivio

Tipologia: Versione Editoriale (PDF)
Dimensione 3.07 MB
Formato Adobe PDF
3.07 MB Adobe PDF   Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11769/321832
Citazioni
  • ???jsp.display-item.citation.pmc??? 3
  • Scopus 13
  • ???jsp.display-item.citation.isi??? 13
social impact