Introduction: The purpose of this study was to assess the effects of sodium hypochlorite (NaOCl) immersion and sterilization on the cyclic fatigue resistance of heat-treated nickel-titanium (NiTi) rotary instruments. Methods: Two hundred ten new 25/.06 Twisted Files (TFs; SybronEndo, Orange, CA) and Hyflex CM (Coltene Whaledent, Cuyahoga Falls, OH) files were divided into 7 groups (n = 15) for each brand. Group 1 (control group) included new instruments that were not immersed in NaOCl or subjected to autoclave sterilization. Groups 2 and 3 were composed of instruments dynamically immersed for 3 minutes in 5% NaOCl solution 1 and 3 times, respectively. Groups 4 and 5 consisted of instruments only autoclaved 1 and 3 times, respectively. Groups 6 and 7 recruited instruments that received a cycle of both immersion in NaOCl and sterilization 1 and 3 times, respectively. Instruments were subsequently subjected to a fatigue test. The surface morphology of fractured instruments was studied by field-emission scanning electron microscopy and x-ray energy-dispersive spectrometric (EDS) analyses. The means and standard deviations of the number of cycles to failure (NCF) were calculated and statistically analyzed using 2-way analysis of variance (P < .05). Results: Comparison among groups indicated no significant difference of NCF (P > .05) except for the groups of TFs sterilized 3 times without and with immersion in NaOCl (P < .05). HyFlex CM files exhibited higher cyclic fatigue resistance than TFs when files were sterilized 3 times, independently from immersion in NaOCl (P < .05). EDS analysis showed the presence of an oxide-rich layer on the Hyflex CM files' external surface. No morphologic or chemical differences were found between files of the same brand subjected to different treatments. Conclusions: Repeated cycles of sterilization did not influence the cyclic fatigue of NiTi files except for TFs, which showed a significant decrease of flexural resistance after 3 cycles of sterilization. Immersion in NaOCl did not reduce significantly the cyclic fatigue resistance of all heat-treated NiTi files tested.
|Titolo:||Cyclic Fatigue Resistance of Heat-treated Nickel-titanium Instruments after Immersion in Sodium Hypochlorite and/or Sterilization|
PEDULLA', EUGENIO [Writing – Original Draft Preparation] (Corresponding)
RAPISARDA, Ernesto [Methodology]
|Data di pubblicazione:||2018|
|Appare nelle tipologie:||1.1 Articolo in rivista|