Study of the crystallization of an aromatic poly-ether-ketone (PK99) by calorimetric and X-ray analysis

An analysis of the crystallization behaviour of a new poly(aryl-ether-ether-ketone-ketone), PK99, by differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) is presented. Isothermal crystallization TG were obtained in the whole range between the glass transition temperature (Tg) and the melting temperature (Tm) as a consequence of the slow crystallization kinetics stemming from the closeness of these transitions. The calorimetric results, compared with WAXD data, were applied to determine the theoretical melting temperature and crystallization enthalpy. The DSC and WAXD data were combined in order to calculate the total amount of the crystallizable fraction of the polymer, and a model was proposed to explain the difference between the fractions of crystallinity observed with these techniques. The thermal and X-ray data were also correlated with different lamellar morphologies arising from the crystallization conditions. Finally, DSC experiments on the crystallized sample were used to detect the presence of a rigid amorphous phase which does not relax at Tg.