The aim of this article is to investigate the interfacial adhesion of Ni-Ti shape memory alloy with a polymer matrix of Poly (methyl methacrylate) (PMMA). The surface pattern on Ni-Ti plates was channeled by a solid state laser machine. The laser machine allows for creating channels on the Ni-Ti surface for infiltration of the PMMA matrix, which could be attached as an intra-surface locking pattern to the Ni-Ti surface. The influence of the PMMA matrix on the surface of the NiTi plate was evaluated by thermomechanical analysis (TMA) and dynamic mechanical analysis (DMA). The surface characterization was carried out by an optical microscope on the PMMA/NiTi composite after mechanical testing. During mechanical testing, the polymer displays the multiple cracks in the longitudinal direction that result in slipping and fracture. TMA and DMA analyses were performed on the Ni-Ti- and PMMA-coated Ni-Ti ribbon to observe elasticity and the storage modulus for both samples. Better adhesion than 80 % was observed in the Ni-Ti surface, in the laser surface pattern, in comparison to the free plain surface. However, the polymer acts as mechanical backing that caused a reduction in the shape-memory properties of the composite material.

Study of Interfacial Adhesion between Nickel-Titanium Shape Memory Alloy and a Polymer Matrix by Laser Surface Pattern

Ignazio Blanco
2020-01-01

Abstract

The aim of this article is to investigate the interfacial adhesion of Ni-Ti shape memory alloy with a polymer matrix of Poly (methyl methacrylate) (PMMA). The surface pattern on Ni-Ti plates was channeled by a solid state laser machine. The laser machine allows for creating channels on the Ni-Ti surface for infiltration of the PMMA matrix, which could be attached as an intra-surface locking pattern to the Ni-Ti surface. The influence of the PMMA matrix on the surface of the NiTi plate was evaluated by thermomechanical analysis (TMA) and dynamic mechanical analysis (DMA). The surface characterization was carried out by an optical microscope on the PMMA/NiTi composite after mechanical testing. During mechanical testing, the polymer displays the multiple cracks in the longitudinal direction that result in slipping and fracture. TMA and DMA analyses were performed on the Ni-Ti- and PMMA-coated Ni-Ti ribbon to observe elasticity and the storage modulus for both samples. Better adhesion than 80 % was observed in the Ni-Ti surface, in the laser surface pattern, in comparison to the free plain surface. However, the polymer acts as mechanical backing that caused a reduction in the shape-memory properties of the composite material.
2020
adhesion; NiTi plate; polymer; PMMA/NiTi composites; mechanical properties; surface features
File in questo prodotto:
File Dimensione Formato  
102.pdf

accesso aperto

Descrizione: articolo principale
Tipologia: Versione Editoriale (PDF)
Dimensione 5.1 MB
Formato Adobe PDF
5.1 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11769/392701
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 20
  • ???jsp.display-item.citation.isi??? 17
social impact