Several aromatic polyamides were prepared from 4,4′-[sulfonyl bis(p-benzoyl)(p-phenyleneoxy)]dibenzoic acid with various diamines by the phosphorylation route. The polymers were characterized by elemental analysis, thermogravimetric analysis, differential scanning calorimetry and infra-red analysis. The polyamides, obtained in quantitative yield, possessed inherent viscosities in the range 0.3-1 dlg-1 and 10% weight loss in nitrogen and air were above 460 and 440°C, respectively. Most of the polymers were soluble in aprotic solvents. The effect of the structure on properties such as solubility and thermal behaviour were also studied
New Aromatic Polyamide Materials Containing Sulphone, Ether and Ketone Linkages
DI PASQUALE, Giovanna;POLLICINO, Antonino;
1996-01-01
Abstract
Several aromatic polyamides were prepared from 4,4′-[sulfonyl bis(p-benzoyl)(p-phenyleneoxy)]dibenzoic acid with various diamines by the phosphorylation route. The polymers were characterized by elemental analysis, thermogravimetric analysis, differential scanning calorimetry and infra-red analysis. The polyamides, obtained in quantitative yield, possessed inherent viscosities in the range 0.3-1 dlg-1 and 10% weight loss in nitrogen and air were above 460 and 440°C, respectively. Most of the polymers were soluble in aprotic solvents. The effect of the structure on properties such as solubility and thermal behaviour were also studiedFile in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.