An analysis of the shape memory effect of a NiTi alloy by using the spark plasma sintering approach has been carried out. Spark plasma sintering of Ti50Ni50 powder (20–63 µm) at a temperature of 900 °C produced specimens showing good shape memory effects. However, the sample showed 2.5% porosity due to a load of 48 MPa. Furthermore, an apparent shape memory effect was recorded and the specimens were characterized by uniformity in chemical composition and shape memory alloys of NiTi showed significant austenite phases with a bending strain recovery of >2.5%
Net-Shape NiTi Shape Memory Alloy by Spark Plasma Sintering Method
Lorenzo Abate;Ignazio Blanco
2021-01-01
Abstract
An analysis of the shape memory effect of a NiTi alloy by using the spark plasma sintering approach has been carried out. Spark plasma sintering of Ti50Ni50 powder (20–63 µm) at a temperature of 900 °C produced specimens showing good shape memory effects. However, the sample showed 2.5% porosity due to a load of 48 MPa. Furthermore, an apparent shape memory effect was recorded and the specimens were characterized by uniformity in chemical composition and shape memory alloys of NiTi showed significant austenite phases with a bending strain recovery of >2.5%File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
125.pdf
accesso aperto
Descrizione: articolo principale
Tipologia:
Versione Editoriale (PDF)
Dimensione
4.91 MB
Formato
Adobe PDF
|
4.91 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.