In straight-wire mechanics, friction can significantly influence the forces expressed by wires. The aim of this study is to assess whether the aging and the sum of elastomeric ligatures affect the static friction during orthodontic space closure. A 0.017x 0.025-in SS was drawn throughout a 3-bracket experimental model and engaged with elastomeric ligatures. Before performing the test, the ligatures were soaked in artificial saliva for 48 hours (Group 1), 2 weeks (Group 2) and 4 weeks (Group 3); brand-new ligatures were also tested as control group (Group 4). The resistance to sliding (RS) was recorded at 3 different numerical configurations of ligatures using a customized testing machine and tests were repeated for ten times. Data of RS were statistically analysed by using two way analysis of variance (ANOVA) and Tukey's multiple comparison tests. RS was found to increase systematically when more elastomeric ligatures were included in the wire engaging system. At two weeks of immersion in artificial saliva elastomeric ligatures showed the lowest values of RS while they became significantly more frictional after immersion for 4 weeks. The results of this study showed that in multi-bracket orthodontic therapy, the RS increases with the number of elastomeric ligatures involved for arch-wire engagement. Differently from the frictional behavior of elastomeric modules, the aging of these ligatures does not influence their incremental effect of frictional forces.

Is static friction affected by aging and amount of elastomeric ligatures in orthodontic sliding mechanics? An in-vitro investigation

Lo Giudice A
Primo
Writing – Original Draft Preparation
;
2018-01-01

Abstract

In straight-wire mechanics, friction can significantly influence the forces expressed by wires. The aim of this study is to assess whether the aging and the sum of elastomeric ligatures affect the static friction during orthodontic space closure. A 0.017x 0.025-in SS was drawn throughout a 3-bracket experimental model and engaged with elastomeric ligatures. Before performing the test, the ligatures were soaked in artificial saliva for 48 hours (Group 1), 2 weeks (Group 2) and 4 weeks (Group 3); brand-new ligatures were also tested as control group (Group 4). The resistance to sliding (RS) was recorded at 3 different numerical configurations of ligatures using a customized testing machine and tests were repeated for ten times. Data of RS were statistically analysed by using two way analysis of variance (ANOVA) and Tukey's multiple comparison tests. RS was found to increase systematically when more elastomeric ligatures were included in the wire engaging system. At two weeks of immersion in artificial saliva elastomeric ligatures showed the lowest values of RS while they became significantly more frictional after immersion for 4 weeks. The results of this study showed that in multi-bracket orthodontic therapy, the RS increases with the number of elastomeric ligatures involved for arch-wire engagement. Differently from the frictional behavior of elastomeric modules, the aging of these ligatures does not influence their incremental effect of frictional forces.
File in questo prodotto:
File Dimensione Formato  
JBRHA 2018 Ligatures.pdf

non disponibili

Tipologia: Versione Editoriale (PDF)
Dimensione 530.39 kB
Formato Adobe PDF
530.39 kB Adobe PDF   Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11769/543295
Citazioni
  • ???jsp.display-item.citation.pmc??? 1
  • Scopus 2
  • ???jsp.display-item.citation.isi??? ND
social impact